厂家(产地) | 埃克森美孚 | 牌号 | 0201 |
断裂伸长率 | 1144 | 规格级别 | 通用 |
拉伸强度 | 30.7 | 密度 | 0.902 |
熔体流动速率 | 2.5 | 弯曲模量 | 67.9 |
产品参数性能项目试验条件[状态]测试方法测试数据数据单位雾度240 milASTM D-100376.1%硬度2Shore A 15 secASTM D-2240>90密度 ExxonMobil Method0.902g/cm3熔体流动速率 ExxonMobil Method2.5g/10 min硬度2Shore D 15 secASTM D-224036.8熔融指数 ExxonMobil Method1.1g/10 min弯曲模量1% secantASTM D-7909842(67.9)psi(MPa)冲击强度23℃ASTM D-256No Breakft-lb/in(J/m)冲击强度-40℃ASTM D-256No Breakft-lb/in(J/m)拉伸强度3@BreakASTM D-638No Breakpsi(MPa)拉伸率@BreakASTM D-638No Break%最高熔体温度 ExxonMobil Method206.4(96.9)?H(℃)维卡软化点21000gASTM D-1525182.7(83.7)H(℃)维卡软化点2200gASTM D-1525205.2(96.2)H(℃)拉应力5@100% ElongationASTM D-4121780(12.3)psi(MPa)拉伸率@BreakASTM D-4121144%抗扯强度 ASTM D-624508.5(89.1)lb-in(kN/m)拉伸强度@PeakASTM D-4124454(30.7)psi(MPa)门尼粘度ML(1+4)125℃ASTM D-16463.9Torgue Units抗环境应力开裂性 ASTM D-1693>1000hr拉应力5@300% ElongationASTM D-4122115(14.6)psi(MPa)